2×4.0mm²-Black/Red (H1Z2Z2-K) Twin Core Solar (PV) Cable (NO.7194103)- IEC62930/EN50618:2014
Product Description
2×4.0mm⊃2;-Black/Red (H1Z2Z2-K) | |||||||
General characteristics: | |||||||
Appllcation: | |||||||
Specifically designed to connect photovoltaic system components inside and outside buildings | |||||||
Cable Construction： | |||||||
Conductor | |||||||
Metarial： | Tinned annealed copper | ||||||
Area(mm⊃2;) : | 2×4.0 | ||||||
Construction(N/mm) : | 56/0.285±0.005 | ||||||
Stranded diameter(mm) : | 2.463 (Ref.) | ||||||
Insulation | 125℃ XLPE Black | ||||||
Min. thickness (mm) : | 0.7 | ||||||
Nom. thickness (mm) : | 0.8 (Ref.) | ||||||
Standard diameter (mm) : | 4.05±0.1 | ||||||
Jacket | 125℃ XLPE, Black/Red | ||||||
Min. thickness (mm) : | 0.7 | ||||||
Nom. thickness (mm) : | 0.8 (Ref.) | ||||||
Outer diameter (mm) : | （5.70±0.10）×（11.5±0.10） | ||||||
Making | ZION COMMUNICATION TÜV SÜD IEC62930 | ||||||
Package： | |||||||
100M/Roll, 500M/Wooden Drum | |||||||
PALLET | |||||||
Electrical properties | |||||||
Nominal Voltage: | H1Z2Z2-K: DC 1.5KV AC 1.0/1.0KV | ||||||
Ambient Temperature: | -40℃~+90℃ | ||||||
Max.Temperature at conductor: | +125℃ | ||||||
Service life: | ＞25 years ( -40℃~+90℃) | ||||||
Voltage: | 600/1000V | ||||||
Temperature: | -40~90℃ | ||||||
Conductor resistance (20℃): | 5.09Ω/km | ||||||
Insulation resistance (70℃): | ≥1000 MΩ/km | ||||||
Withstand voltage(V/5min) | AC6500 | ||||||
Speak voltage(V/5min) | AC6500 | ||||||
Min bending radius(mm) | 4*D | ||||||
Main performance parameter of finished cable | |||||||
Voltage test of finished cable | |||||||
Min.time of dipping in water | ≥1(h) | ||||||
Testing voltage (AC) | 6500(V) | ||||||
Min.voltage applying time at one time | 5(min) | ||||||
Test result | no breakdown | ||||||
Sheated surface resistance | |||||||
Length of specimen: | 250mm | ||||||
Test result | ≥109Ω | ||||||
Penetrate the insulation resistance | |||||||
Temperature | 20℃ | ||||||
Test result | ≥1014Ω | ||||||
High temperature stress | |||||||
Temperature | 140℃ | ||||||
A: with 1.2 Voltage test | A: No breakdown | ||||||
B: deep pressure | B: Wall thickness 50% | ||||||
Damp-heat test | |||||||
Temperature | 90℃ | ||||||
Humidity | 85% | ||||||
Aging before and after the tenslle strength of Change | ≤30% | ||||||
Aging before and after the elongation at break of Change | ≤-30% | ||||||
Acid-alkali Resistance | |||||||
Min.time of dipping in | 168h | ||||||
Aging before and after the tensile strength of Change | ≤-30% | ||||||
Elongation | ≥100 | ||||||
Low-temperature bending | |||||||
Temperature | -40℃ | ||||||
Time | 16h | ||||||
Test result | No crack | ||||||
Ozone resistance | |||||||
Ozeone concentration % | （200±50）x10-6 | ||||||
Time | 72h | ||||||
Test result | No crack | ||||||
Heat schrinkable jacket test | |||||||
Test result | ≤2% | ||||||
Flame retardant-Vertical burn | |||||||
Flxture on the lower edge from the starting point and carbonization | ≥50mm | ||||||
Burning fuel downward from the lower edge of bottom fixture | ≤540mm | ||||||
Halogen content of non-metallic materials | |||||||
Test result | |||||||
Chlorine and bromine content | HCL≤0.5HBr≤0.5% | ||||||
Fluoride content | F≤0.1% | ||||||
The inner layer of insulation and sheath of the mechanical properties | |||||||
Test result | |||||||
Aging before tensile strength | 8.0N/mm⊃2; | ||||||
Aging before elongation | 1.25 | ||||||
Aging before and after the tensile strength of change | -0.3 | ||||||
Aging before and after the elongation at break of change | -0.3 | ||||||
Hot extension | |||||||
Temperature | 200℃ | ||||||
Test result-The inner layer of insulation and sheath | |||||||
Elongation under load | ≤100% | ||||||
Elongation after unloading | ≤25% | ||||||