16mm²-B (PV1-F / H1Z2Z2-K) Single core Solar Cable

  • Solar cable

  • hellosignal

  • NO.7194005

  • Power Cables

  • Normally 25 working days

  • NINGBO, SHANGHAI

Availability:

Product Description

16mm²-B (PV1-F / H1Z2Z2-K)
NO.7194005

General characteristics:

 General characteristics

Appllcation:

Specifically designed to connect photovoltaic system components inside and outside buildings
and facilities under high mechanical demands and extreme weather conditions.

Cable Construction:

Conductor



Solar Cable 

Metarial

Tinned annealed copper

Area(mm²) :

1*16

Construction(N/mm) :

128/0.40

Conductor(Dia./mm) :

5.25


 

Insulation

120℃ XLPE

Standard thickness (mm) :

0.9

Standard diameter (mm) :

7.05±0.1

Jacket

120℃ XLPE, Black

Standard thickness (mm) :

1.2

Outer diameter (mm) :

9.45±0.2

Making

ZION COMMUNICATION PV1-F / H1Z2Z2-K 1x16mm² UV Res
DC 1.0KV AC 0.6/1.0KV (DC 1.5KV AC 1.0/1.0KV)
SOLAR CABLE








Package

BOX  (art.code ZC-100-16mm/ZC-500-16mm)     


package 


PALLET     

Size:     

Amount of boxes on one pallet:


Weight of total pallet:


Cable length pallet:



Electrical properties

Nominal Voltage:

PV1-F:          DC 1.0KV   AC 0.6/1.0KV
H1Z2Z2-K:   DC 1.5KV   AC 1.0/1.0KV

Ambient Temperature:

-40℃~+90℃

Max.Temperature at conductor:

+120℃

Service life:

25 years ( -40~+90℃)

Conductor resistance (20℃):

1.24Ω/km

Insulation resistance (70℃):

≥1000 MΩ/km

Withstand voltage(V/5min)

AC6500

Speak voltage(V/5min)

AC6500

Min bending radius(mm)

5*D


Main performance parameter of finished cable

Voltage test of finished cable

Min.time of dipping in water

≥1(h)

Testing voltage (AC)

6500(V)

Min.voltage applying time at one time

5(min)

Test result

no breakdown

Sheated surface resistance

Length of specimen:

250mm

Test result

≥109Ω

Penetrate the insulation resistance

Temperature

20℃

Test result

≥1014Ω

High temperature stress

Temperature

140℃

A: with 1.2 Voltage test

A: No breakdown

B: deep pressure

B: Wall thickness 50%

Damp-heat test

Temperature

90℃

Humidity

85%

Aging before and after the tenslle strength of Change

≤30%

Aging before and after the elongation at break of Change

≤-30%


Acid-alkali Resistance

Min.time of dipping in

168h

Aging before and after the tensile strength of Change

≤-30%

Elongation

≥100

Low-temperature bending

Temperature

-40℃

Time

16h

Test result

No crack

Ozone resistance

Ozeone concentration %

200±50x10-6

Time

72h

Test result

No crack

Heat schrinkable jacket test

Test result

≤2%

Flame retardant-Vertical burn


Flxture on the lower edge from the starting point and carbonization

≥50mm

Burning fuel downward from the lower edge of bottom fixture

≤540mm

Halogen content of non-metallic materials

Test result


Chlorine and bromine content

HCL≤0.5HBr≤0.5%

Fluoride content

F≤0.1%

The inner layer of insulation and sheath of the mechanical properties

Test result


Aging before tensile strength

8.0N/mm²

Aging before elongation

125%

Aging before and after the tensile strength of change

-30%

Aging before and after the elongation at break of change

-30%

Hot extension

Temperature

200℃

Test result-The inner layer of insulation and sheath


Elongation under load

≤100%

Elongation after unloading

≤25%










Previous: 
Next: 
We use cookies to enable all functionalities for the best performance during your visit and to improve our services by giving us some insight into how the website is being used. Continued use of our website without changing your browser settings confirms your acceptance of these cookies. For details, please see our privacy policy.
×